DWH 314 CS is a low-viscosity adjustment and filling resin in a double cartridge for casting and injection, designed for form- and forcefitting filling and gluing of joints on components, assemblies of different materials. Due to spatula- and molding techniques it is possible to even achieve precision in µm-range. When using a micro-thin layer of DIAMANT-parting agent on the counter surface DWH 314 CS can be seperated from it. The result is an exact copy of the molded surface. A high-perision preperation of surfaces and the mechanical post-processing of the surfaces is not necessary. In modern production processing times and costs can be dramatically reduced.

Typical applications

  • non-magnetic
  • does not contain metallic fillers
  • Form- and force-fitting installation of guides in mechanical engineering
  • Adjusting coating for assemblies and elements of various materials.
  • Full-surface lining of mouldings and elements as a replacement for feed plates.
  • Load-bearing gap compensation on beams of portal milling and gantry systems
  • μm- precise fitting of bushes, centering and guide elements
  • Fixing and / or centering of bearing bushes according to high precision alignment
  • As filling and composite material in 3D printing + Additive Manufacturing


  • Very high accuracy, μm-accurate moulding
  • Very high compressive strenght
  • Extreme dimensional stability  after curing
  • Excellent load transfer due to complete application of the contact surfaces
  • Temperature resitant up to +80 °C
  • Excellent damping properties thanks to the E-module ca. 8300 N/mm²
  • mineral-anthracite color after curing
  • High resistance against oils, cooling emulsions, mineral and synthetic coolants and lubricants and many other chemicals.

Chemical resistance

Please contact our technicians for questions about chemical resistance.

Storage / Shelf life

Store in original, unopened container in a dry, cool and frost-free place (+5°C to +20°C). Shelf life 2 years. Keep away from direct sunlight. Higher temperatures reduce the shelf life.

Preparation of the bonding surface

The surfaces to be coated should have a significant roughening to improve adhesion. The peak-to-valley height should be 0.5 mm (Rt = 500μm). The roughening can be produced, for example, with a cutter head with a large feed on a milling machine.surfaces must be clean, dry and free of grease and oil. For cleaning dirty surfaces we recommend DIAMANT Cleaner #1417 or DIAMANT Cleaning Spray #1534.Surfaces to which DWH should not adhere should be coated with Release Agent #1354 or Release Spray #1355.

Mixing Procedure

To mix DWH 314 P, add Component B completely to the Component A container. Mix intensively with a drill and the DIAMANT mixing propeller (Prod. No. #0789) (max. 250 rpm for approx. 2 minutes). Scrape off any material adhering to the wall of the container with a spatula and add to the mixture. Mix again thoroughly. The deaeration described below also results in a final mixing.


Remove DWH 314 P from the container immediately after mixing and spread thinly, crosswise, on a clean sheet. By spreading, a further mixing effect is achieved, but in particular stirred-in air bubbles are broken up. furthermore, a part of the reaction heat is dissipated by spreading over the surface, whereby the processing time is secured.

Description of use

First apply DWH 314 P with a trowel as a thin adhesive layer firmly onto the adhesive primer.Further trowel the product on the roof with a small excess without trapping air.The excess quantity applied should displace the air when moulding the components and thus ensure bubble-free application.

Technical data sheet for DIAMANT 314 CS